ASTM G Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens. ASTM G(). Standard Practice for Making and Using C-Ring Stress- Corrosion Test Specimens. standard by ASTM International. Find the most up-to-date version of ASTM G38 at Engineering

Author: Vora Kazrakree
Country: Turkey
Language: English (Spanish)
Genre: Health and Food
Published (Last): 22 March 2008
Pages: 385
PDF File Size: 5.92 Mb
ePub File Size: 19.92 Mb
ISBN: 149-9-36521-303-7
Downloads: 17229
Price: Free* [*Free Regsitration Required]
Uploader: Doumi

Therefore, to conduct tests aatm SCC, either mechanical or electrochemical means are often utilized to promote localized corrosion so that the inherent susceptibility of the material can be determined.

Under the sleeve, evidence of severe general and pitting corrosion were found and evidence of sulfur-containing corrosion products. ASTM G – practice for evaluation of scc resistance of metals and alloys in 3.

ASTM G – practice for preparation and use of direct tension scc test specimens. Touchstone Research Laboratory, Ltd.

ASTM G38 – 01() Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens

ASTM G – practice for preparation of scc test specimens for weldments. ASTM G – practice for preparation and use of bent-beam scc test specimens. Stress of principal interest in the C-ring specimen is b38 circumferential stress because this stress is not uniform. Analysis of the elastomer indicate that it was not the correct grade and chemical degradation had occurred in service to produce organic acids and sulfur compounds.

Due to the very large number of tests offered, descriptions of those most commonly requested have been gathered g338 the following groups: Please email info trl.

  EXTRACCION DE BIXINA PDF

Select from list below: SCC is the brittle cracking of a h38 due to the result of combined effects from localized corrosion and tensile stress. Touchstone takes care that the specimens are supported by nothing more than the corrosive medium comes into contacted with the critically stressed area of the specimen.

Touchstone Engineers have experience with Stress-Corrosion Testing and are able to accurately determine when the specimen fractured and obtain a precise cracking time. To request a quotation for any test email info trl.

When the specimen is stressed by measuring the strain on the tension surface of the c-ring, the strain gage should be positioned in the middle of the arc in order to indicate the maximum strain. Prevention or Remedial Action.

Care must be taken during machining so that specimens are not overheated, are not plastically deformed and do not develop residual stresses in the metal surface. In some cases, where constant load tests are used, environmental cracks can initiate but not propagate through the entire cross-section of the specimen. ASTM D steels caustic.

Therefore, the specimen may not fail, but significant cracking may take place. An analysis is given of the state and distribution of stresses in the C-ring. This local environment resulted in enhanced asrm susceptibility of the material to pitting corrosion and SCC.

These are typical of stress corrosion cracking SCC in austenitic stainless steel. Stress Corrosion Cracking of Stainless Steel – The example shown indicates many intersecting, branched cracks with a transgranular propagation mode.

In many cases, SCC involves the combination of tensile stress and local anodic attack which dictate the period of incubation prior to the initiation of SCC. Stress Corrosion Cracking Stress Corrosion Testing Description SCC is the brittle cracking of a metal due to the result of combined effects from localized corrosion and tensile stress. This practice covers the features of design and machining, and procedures for stressing, exposing, and inspecting C-ring type of stress-corrosion test specimens.

  LM380N DATASHEET PDF

In this case, however, the alloy was reported to be resistant to SCC in the NaCl brine service environment.

ASTM G38 – Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens

ASTM F titanium aircraft engine cleaning materials. Prevention or Remedial Action lower either applied or residual tensile stresses. The location of cracking was limited to a region covered by an elastomeric sleeve. The example shown indicates many intersecting, branched cracks with a transgranular propagation mode. There are also transverse stresses present; however, g388 stresses may decrease with decreasing width to thickness and increasing diameter to thickness ratios.

ASTM G38 – 01 Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens

Such techniques include the use of slow strain rate, cyclic slow strain rate, fracture mechanics and electrochemical wstm control. Determination of the cracking time may be subjective due to the visual examination.

Stress Corrosion Cracking of Stainless Steel. Due to the very large number of asym offered, descriptions of those most commonly requested have been gathered into the following groups:.